Fabrication and Characterization of Antibacterial Suture Yarns Containing PLA/Tetracycline Hydrochloride-PVA/Chitosan Nanofibers 


Vol. 23,  No. 6, pp. 1538-1547, Jun.  2022
10.1007/s12221-022-4685-z


PDF
  Abstract

Antibacterial suture yarns containing antibiotic drugs can play an important role in preventing the infection and holding tissues together to achieve wound closure. In this research, the possibility of production drug loaded nano yarns from a mixture of chitosan/polyvinyl alcohol (PVA/CS) (70:30) and poly(lactic acid) (PLA) was assessed by combining dual릂lectrospinning technique with aligned fibers collection. For this, CS/PVA solution was injected from one syringe and PLA from another one. The effect of weight ratio of PLA-PVA/CS (100:0, 80:20 and 60:40), collector speed (500, 800, 1100 rpm) and voltage (10, 15 and 20 kV) on the diameter and morphology of fabricated nanofibers was assessed. Fabricated nanofibers with the length of 70 cm were twisted for manufacturing suture yarns. The results showed that fabrication of structure with the finest diameter was possible with the weight ratio of PLA-PVA/CS (60:40), the applied voltage of 15 kV, spinning distance of 17 cm and the rotational speed of about 1100 rpm. The diameter of produced nanofibers in this condition was about 290짹42 nm. Then, tetracycline hydrochloride (T) loaded PLA-PVA/CS nanofibers (PLA/T-PVA/CS) were produced with optimum condition and the drug (5 wt. %) was loaded in PLA solution. FTIR analysis of drug loaded yarn exhibited the most important functional groups of chitosan, PVA, tetracycline hydrochloride and PLA in PLA-PVA/CS structure. Contact angle data for PLA-PVA/CS and PLA/T-PVA/CS was about 89짹3 째 and 30짹2 째, respectively. The result of the antibacterial test indicated that the PLA/T-PVA/CS nanofibrous yarns were the most suitable sample with the prominent antibacterial activity against both gram-positive bacterium Staphylococcus aureus and gram-negative bacterium Escherichia coli with inhibition zones of 17.5 and 20 mm, respectively. It seems that the fabricated nanofiber based yarns with suitable morphological characteristics, hydrophilicity nature, and prevention of the surgical infections without affecting the cell viability can be an excellent structure for utilization as suture yarn.

  Statistics
Cumulative Counts from November, 2022
Multiple requests among the same browser session are counted as one view. If you mouse over a chart, the values of data points will be shown.


  Cite this article

[IEEE Style]

M. Ranjbar-Mohammadi, V. Sa셝i, M. Moezzi, R. Saghafi, "Fabrication and Characterization of Antibacterial Suture Yarns Containing PLA/Tetracycline Hydrochloride-PVA/Chitosan Nanofibers," Fibers and Polymers, vol. 23, no. 6, pp. 1538-1547, 2022. DOI: 10.1007/s12221-022-4685-z.

[ACM Style]

Marziyeh Ranjbar-Mohammadi, Vida Sa셝i, Meysam Moezzi, and Reza Saghafi. 2022. Fabrication and Characterization of Antibacterial Suture Yarns Containing PLA/Tetracycline Hydrochloride-PVA/Chitosan Nanofibers. Fibers and Polymers, 23, 6, (2022), 1538-1547. DOI: 10.1007/s12221-022-4685-z.

Search
(IN TITLE, AUTHOR, ABSTRACT,KEYWORDS)

Advanced Search ▼

POPULAR KEYWORDS
(TOP 10 KEYWORDS)

Recent Publications
(LAST 3 YEARS)

pISSN : 1229 - 9197
eISSN : 1875 - 0052

Impact Factor(2024): 2.3